Co-sintered surface metallization for pin-join, wire-bond and chip attach

ABSTRACT

A co-sintered ceramic substrate structure is formed through punching and screening of a plurality of ceramic green sheets with a plurality of composite metal pastes and/or inks and laminating the structure. The co-sintered surface metallization comprises dual screened composite metal pastes, one on top of the other and bonded to the sintered ceramic substrate to provide bonding of the surface metallization to the sintered ceramic substrate.

CROSS REFERENCE TO RELATED APPLICATION

This application is a divisional of application Ser. No. 08/360,526 filed Dec. 21, 1994.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention generally relates to the field of pin joining, wire bonding and chip attachment to ceramic structures, and their manufacture, and more particularly to multilayer ceramic substrates for mounting semiconductor devices. In such applications, co-sintering the surface metallization to facilitate direct pin joining, wire bonding and chip attachment hold significant advantages.

2. Description of the Prior Art

The current art for surface metallization of glass ceramic is done by lithography and thin film evaporation and sputtering on planarized surfaces. The need for a planar surface for lithography and thin film processes warrants surface machining of sintered ceramic, and such planarization processes are very expensive manufacturing operations.

For substrates having alumina as the ceramic, the metallization is usually molybdenum (Mo) or tungsten (W). The surface metal features are bonded to the ceramic by the addition of glasses. Subsequent joining of pins, wires and chips to these refractory metal features is done after plating of nickel on Mo-glass or W-glass composite.

In the case of low temperature sinterable glass ceramics, the metallic conductors used are traditionally copper, silver or gold. The bonding of surface metal features to glass ceramic substrates is more difficult due to large thermal expansion mismatch between the substrate and the metal. One approach for surface metallization of glass ceramic is to deposit thin film features either by evaporation or sputtering. This requires planar surfaces and hence involves surface machining which makes it very expensive. Various class ceramic compositions are disclosed in U.S. Pat. No. 4,413,061 to Kumar et at. Sintering cycles using hydrogen and water vapor have been taught in U.S. Pat. No. 4,234,367 to Herron et at. This is done at low temperatures to remove binders.

SUMMARY OF THE INVENTION

It is therefore an object of the present invention to provide co-sintered surface metallization on ceramic substrate surfaces and methods of manufacturing the same for use in electronic applications.

It is another object of the present invention to provide surface metallization on ceramic substrates without expensive lapping and polishing.

It is further an object of the present invention to provide a method for achieving direct pin-attach, wire-bond and chip-attach, such that surface finishing of the sintered ceramic and/or lithographic or thin film metallization is eliminated.

According to the invention, a co-sintered ceramic substrate structure is formed through punching and screening of a plurality of ceramic green sheets with a plurality of composite metal pastes and/or inks and laminating the structure. A glass ceramic substrate comprising a metal paste of 40% by volume of copper and 60% by volume of glass as disclosed in U.S. Pat. No. 5,073,180 to Farooq et al., the disclosure of which is incorporated by reference herein, is preferably used in a first layer. A second layer including nickel is applied over the first layer. The co-sintered surface metallization comprises dual screened composite metal pastes, one on top of the other and bonded to the sintered ceramic substrate. Accordingly, it is yet another object of the present invention to provide bonding of the surface metallization to the sintered ceramic substrate.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other objects, aspects and advantages will be better understood from the following detailed description of a preferred embodiment of the invention with reference to the drawings, in which:

FIG. 1 is a cross-sectional view showing a stack of ceramic green sheets with top ceramic layer screened first with composite metal paste for surface metallization following by a second surface metal paste; and

FIG. 2 is a cross-sectional view showing a sintered ceramic substrate with the co-sintered surface metallization and pin attached metal structure.

DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT OF THE INVENTION

Referring now to the drawings, and more particularly to FIG. 1, there is shown a plurality of ceramic green sheets 1, which are punched forming vias and screened with metal pastes for electronic applications forming a capture pad. A copper/glass composite paste, such as has been disclosed in U.S. Pat. No. 5,073,180 to Farooq et al., has been screened onto the green sheets 1 partially filling the punch hole 3 and forming a first layer 2. A second layer 4 of metal paste is deposited on top of the first layer 2. Table 1 below outlines 3 combinations of which the first and second layers may consist. In Table 1, the preferred composition of the first layer is 40% by volume of copper and 60% by volume of glass of the glass/copper composite with copper and glass particle sizes taught in the patent to Farooq et al.

                  TABLE 1                                                          ______________________________________                                                                           bonding                                      combination                                                                             first layer                                                                               second layer  atmosphere                                   ______________________________________                                         1        screened   screened nickel                                                                              99% stream                                            glass/copper                                                                              paste         1% hydrogen                                           composite                                                             2        screened   screened (vol. %)                                                                            99.75% steam                                          glass/copper                                                                              copper (88%) and                                                                             0.25%                                                 composite  nickel (12%) paste                                                                           hydrogen                                     3        screened   screened (vol. %)                                                                            99.5 % steam                                          glass/copper                                                                              copper (80%) and                                                                             0.5%                                                  composite  nickel (20%) paste                                                                           hydrogen                                     ______________________________________                                    

The pastes which comprise the first and second layers are composed of substances which may have different coefficients of expansion from the ceramic green sheet. The first layer is formulated such that it remains bonded (in contact) with the ceramic after sintering and no gaps are formed between the ceramic and the first layer. The first layer, because of its composite nature, is closer in coefficient of expansion to that of the glass-ceramic. The second layer is likewise formed with respect to the first layer, so that there may be a gradation of coefficients of expansion between the ceramic green sheet and the second layer, but the three materials remain in one structure after sintering. (For example, the coefficient of expansion of glass-ceramic is 3 ppm/°C. and that of glass-ceramic/copper composite is about 7 ppm/°C. The coefficient of expansion of the second layer is in the 13 to 18 ppm/°C. range.)

After the first and second layer pastes are applied, the structure thus far is sintered. Generally speaking, the sintering procedure is done according to the teachings of Farooq et at., U.S. Pat. No. 5,073,180, with a slight change necessary to accommodate the bonding of the first and second layers to the glass ceramic body. Briefly, the structure undergoes pyrolysis, binder burnoff, and densification according to Farooq et al. Then, the atmosphere is changed to one of the atmosphere as shown in Table 1 to accomplish sealing and recrystallization of the glass ceramic substrate and bonding of the surface metallization. This bonding atmosphere is somewhat different from the sealing atmosphere preferred in Farooq et at. Thereafter, the structure is cooled.

The bonding atmosphere is specifically chosen to provide an environment in which residual oxide remains to promote bonding. Changes made in the bonding atmosphere could result in no bonding occurring.

FIG. 2 shows the invention with the co-sintered surface metallization and pin attached. As can be seen in the figure, there is an additional very thin layer of plated gold 5 having thickness of about 1000 Å. The pin head 7 is attached with solder 6, which may be 95% tin and 5% antimony or lead-tin solder.

The invention was tested with a standard pin-pull test. Table 2 shows the results of the pin-pull test.

                  TABLE 2                                                          ______________________________________                                         Structure type pin-pull, lbs                                                                            Total pins                                            ______________________________________                                         1              11.2 ± 0.9                                                                            90                                                    2              10.7 ± 1.0                                                                            104                                                   3              12.0 ± 0.8                                                                            70                                                    ______________________________________                                    

It is best if failure does not occur in the ceramic. With the present invention, failure is expected at four points:

1. At the interface between the ceramic and the copper glass composite 9.

2. At the interface between the copper/glass composite and the copper/nickel or nickel film 10.

3. In the glass ceramic 1.

4. In the pin shank 8.

It is most desirable that failure occur in the pin shank 8. If failure occurs in the pin shank or solder, the solder can be cleaned out and an new pin added. If the gold layer is pulled off, it can be added again followed by replacing the pin and solder. Failure at other interfaces will require the structure to be built again. Failure in this glass ceramic 1 cannot be repaired, thereby necessitating the disposal of the glass-ceramic body. Failure of the structure according to this invention was most often observed at the interface between the copper/glass composite and nickel or copper/nickel film 10. Failure in the pin shank occurs at about 12.5 pounds of force. However, the strengths as shown by Table 2 above were high. No failure was observed in the interface between the ceramic and the copper glass composite 9 or the glass ceramic 1.

The invention is formed by providing ceramic green sheets, stacked and punched. Screening a paste of glass ceramic/copper composite onto the stacked green sheets. Screening a paste of nickel or copper/nickel alloy on the composite. Sintering the structure so that the composite has a total thickness of 6-20 microns and the nickel layer has a total thickness of 6-20 microns. The structure is plated with gold after sintering. The structure is then ready for pin joining, wire bonding, and chip attach. The steps of producing this structure do not require planarization.

While the invention has been described in terms of preferred embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the appended claims. 

Having thus described our invention, what we claim as new and desire to secure by Letters Patent is as follows:
 1. A metallized structure for pin joining, wire bonding, and chip attachment to multilayered ceramic substrates comprising:a multilayered structure comprising a glass-ceramic substrate and first and second metallized layers produced by sintering plurality of stacked ceramic green sheets having at least one via therein, said first metallized layer comprising a glass-ceramic/copper composite and said second metallized layer comprising a metal containing nickel; and nickel/gold or gold plated on said nickel-containing metal and composite.
 2. A metallized structure for pin joining, wire bonding, and chip attachment as in claim 1 wherein the coefficient of expansion of the glass-ceramic substrate is 3 ppm/°C., the coefficient of expansion of the first layer of glass-ceramic/copper is about 7 ppm/°C. and the coefficient of expansion of the second layer containing nickel is in the range of 13 to 18 ppm/°C.
 3. A metallized structure for pin joining, wire bonding, and chip attachment as in claim 1 wherein said nickel-containing metal is nickel.
 4. A metallized structure for pin joining, wire bond, and chip attachment as in claim 1 wherein said nickel-containing metal is a copper and nickel mixture wherein the volume percent of copper is in the range of 80 to 88% and the volume percent of nickel is in the range of 20 to 12%.
 5. A metallized structure for pin joining, wire bond, and chip attachment as in claim 4 wherein said nickel-containing metal is composed of 88% by volume of copper and 12% by volume of nickel.
 6. A metallized structure for pin joining, wire bonding, and chip attachment as in claim 4 wherein said nickel-containing metal is composed of 80% by volume of copper and 20% by volume of nickel. 